Datos del producto:
|
| Usar: | proyecto de hornos de cal y otros hornos | chemicalResistance: | Resistente a escorias ácidas y alcalinas. |
|---|---|---|---|
| Obstinación: | ≥ 1580°C | Contenido de carbono: | 99% |
| Tamaño: | Tamaños estándar como 230x114x65 mm o personalizados | Porosidad: | 10% - 30% |
| Modo de construcción: | Las demás piezas de papel | Temperatura: | 1600 grados |
| Contenido de óxido de calcio: | ≤15% | Nombre de producto: | Los ladrillos refractarios de horno |
| Longitud: | Las medidas de seguridad se aplicarán a las medidas de seguridad. | CENIZA: | 0.3% |
| Tipo: | Enlaces de fosfato | Composición química: | AL2O3-SIO2 |
| servicioVida: | Normalmente entre 3 y 10 años, según el uso. | ||
| Resaltar: | Rongsheng AZS refractory brick,zirconia corundum fused cast block,glass kiln refractory brick |
||
AZS bricks, also known as fused zirconia corundum bricks, are made by carefully selected zircon sand and industrial aluminum oxide powder in a 1:1 ratio, with a small amount of flux added, mixed evenly, melted at 1800~1900 ℃, and then cast into shape. Generally, zirconium corundum bricks can be divided into several grades according to the content of ZrO2, such as three grades of 33%, 36% and 41%. They have high melting point, good chemical stability, and strong corrosion resistance to acid and alkaline media, especially molten glass.
Features of AZS Brick
1.Casted by melting raw material in the mold, then cooling and solidification.
2.Strong glass corrosion resistance and high thermal shock stability.
3.Good wear-resistance,slag-resistance and alkali corrosion resistance.
4.High-purity raw material, barely no pollution.
5.Top quality, long service time.
Shapes and sizes: there are great variety of formats and shapes which are available for different forming and special machine processes.
Applications of AZS Brick
1.Sodium silicate furnace, ceramic frit furnace, glass furnace, etc..
2.Important parts of furnaces where chemical erosion is serious and temperature changes frequently.
3.Lining of glass furnace.
4.The chemical industrial, metallurgical furnaces.
Zirconium Corundum Bricks Properties:
| chemical composition | AZS-33 | AZS-36 | AZS-41 |
| ZrO2 | ≥33 | ≥35 | ≥40 |
| SiO2 | ≤16.0 | ≤14 | ≤13.0 |
| Al2O3 | a little | a little | a little |
| Na2O | ≤1.5 | ≤1.6 | ≤1.3 |
| Fe2O3+TiO2 | ≤0.3 | ≤0.3 | ≤0.3 |
Zirconium Corundum Bricks Physical Properties:
| bulk density(g/cm3): | 3.5-3.6 | 3.75 | 3.90 | |
| cold crushing Mpa | 350 | 350 | 350 | |
| thermal expansion coefficient (1000°C) | 0.80 | 0.80 | 0.80 | |
| exudation temp. of glass phase | 1400 | 1400 | 1400 | |
| corrocion resistance of glass melt(mm/24h) | 1.6 | 1.5 | 1.3 | |
| Density | PT QX | 3.40 | 3.45 | 3.55 |
| WS ZWS | 3.60 | 3.70 | 3.8 | |
Zirconium Corundum Bricks Phase Composition(%):
| baddeleyite | 32 | 35 | 40 |
| glass phase | 21 | 18 | 17 |
| α- corundum | 47 | 47 | 43 |